| NOMINAL | THICKNESS | WEIGHT | WORKING PRESSURE | ||
| inches | inches | mm | lbs/ft | grams/m | psi/bar |
| 6" | 0.19 | 4.8 | 2.01 | 3000 | 930 /64 |
| 7 1/4" | 0.19 | 4.8 | 2.44 | 3640 | 750 /17 |
Longman Hippo shall be made from 100% high tenacity synthetic yarn circular woven and completely, protected and locked-in by tough highly resistant synthetic nitrile rubber, forming a single homogenous construction without the use of glues or adhesives of any type.
The ribs on the cover surface greatly increase abrasion resistance and help provide a long service life.
Standby hoses in nuclear power station
Supply hoses in petrochemical refefineries
Lining Properties:
a. Ultimate Tensile Strength:
Tensile strength of the lining and cover shall not be less than 1500 psi (10,500 kpa ).
b. Ultimate Elongation:
400% minimum.
c. Accelerated Aging Test
The tensile strength and ultimate elongation of the vulcanized rubber compound which has been subjected to the action of oxygen at a pressure of 300 psi +/- 10 psi , (2100kpa +/- 70kpa) and temperature of 70 degrees centigrade +/-1 degree centigrade (158 F +/- 18 F ) for a period of 96 hours shall be , greater than 60% of the original properties stated.
Color:Yellow or Red
Temperature range:-5° to 200°F (-20° to 95°C)
Elongation at WP:<1.5%
Expansion at WP:<4%
Abrasion:6000 DIN cycles
Standard Length: 50ft, 100ft, 20m, 30m
Manufactured in accordance with NFPA 1961 standard, latest edition.
within our ISO-9001 certified quality assurance system.